N-Benzyl-N,N-dimethylhexadecan-1-aminium chloride (cas: 122-18-9) belongs to organic chlorides. Chlorination modifies the physical properties of hydrocarbons in several ways. These compounds are typically denser than water due to the higher atomic weight of chlorine versus hydrogen.While alkyl bromides and iodides are more reactive, alkyl chlorides tend to be less expensive and more readily available. Alkyl chlorides readily undergo attack by nucleophiles.Application In Synthesis of N-Benzyl-N,N-dimethylhexadecan-1-aminium chloride

Engineering titanium carbide ultra-thin nanosheets for enhanced fire safety of intumescent flame retardant polylactic acid was written by Shi, Yongqian;Wang, Zixiao;Liu, Chuan;Wang, Hengrui;Guo, Jin;Fu, Libi;Feng, Yuezhan;Wang, Liancong;Yang, Fuqiang;Liu, Minghua. And the article was included in Composites, Part B: Engineering in 2022.Application In Synthesis of N-Benzyl-N,N-dimethylhexadecan-1-aminium chloride The following contents are mentioned in the article:

As a biodegradable polymeric material, the polylactic acid (PLA) has broad applications resulting from its various advantages and unique characteristics. Nevertheless, the application of PLA in various fields is greatly limited by its high flammability. Our recent effort focuses on the manipulation of benzyldimethylhexadecylammonium chloride (HDBAC) modified titanium carbide (Ti3C2Tx) ultra-thin nanosheets which are then used to improve the fire safety of PLA composites filled with silicon microencapsulated ammonium polyphosphate (SiAPP). The flame retardant evaluation showed that when 2.0 wt% HDBAC modified Ti3C2Tx (HDBAC-Ti3C2Tx) and 13.0 wt% SiAPP were added, the LOI value was increased to 33.3%, and the UL-94 V-0 level was obtained, besides the peak heat release rate, total heat release, peak smoke production rate and total smoke release decreased by 49.8%, 31.9%, 60.3% and 52.7%, resp. The barrier and catalytic effects of the modified Ti3C2Tx nanosheets together with the subsequently formed TiO2 and phosphorus-containing species forming intact expanded carbon layers and interrupting the combustion route are responsible for remarkably improving flame retardancy and suppressing toxic gases of PLA. This work provides a new approach for greatly reducing the fire hazard of PLA. This study involved multiple reactions and reactants, such as N-Benzyl-N,N-dimethylhexadecan-1-aminium chloride (cas: 122-18-9Application In Synthesis of N-Benzyl-N,N-dimethylhexadecan-1-aminium chloride).

N-Benzyl-N,N-dimethylhexadecan-1-aminium chloride (cas: 122-18-9) belongs to organic chlorides. Chlorination modifies the physical properties of hydrocarbons in several ways. These compounds are typically denser than water due to the higher atomic weight of chlorine versus hydrogen.While alkyl bromides and iodides are more reactive, alkyl chlorides tend to be less expensive and more readily available. Alkyl chlorides readily undergo attack by nucleophiles.Application In Synthesis of N-Benzyl-N,N-dimethylhexadecan-1-aminium chloride

Referemce:
Chloride – Wikipedia,
Chlorides – an overview | ScienceDirect Topics